Radilon? S USZ200 100 NAT
Polyamide 6
PA6 injection moulding grade. Toughened. Natural colour.
Suitable for parts requiring excellent impact resistance, even at low temperatures, and high flexibility.
Features | |
RoHS Compliance | |
Appearance | |
Processing Method | |
Resin ID (ISO 1043) | |
Density | 1.06 | -- | g/cm3 | ISO 1183 |
Molding Shrinkage 2 |
|
|
| ISO 294-4 |
Across Flow | 1.4 | -- | % |
|
Flow | 1.5 | -- | % |
|
Water Absorption |
|
|
| ISO 62 |
Saturation, 73°F, 0.0787 in | 7.9 | -- | % |
|
Equilibrium, 73°F, 0.0787 in, 50% RH | 2.0 | -- | % |
|
Tensile Modulus | 232000 | 87000 | psi | ISO 527-2/1A/1 |
Tensile Stress (Yield) | 5800 | 2900 | psi | ISO 527-2/1A/50 |
Tensile Strain (Yield) | 5.0 | 30 | % | ISO 527-2/1A/50 |
Nominal Tensile Strain at Break | > 100 | > 100 | % | ISO 527-2/1A/50 |
Flexural Modulus 3 | 203000 | -- | psi | ISO 178 |
Flexural Stress 3 | 7980 | -- | psi | ISO 178 |
Charpy Notched Impact Strength |
|
|
| ISO 179/1eA |
-22°F | 40 | -- | ft·lb/in2 |
|
73°F | 43 | -- | ft·lb/in2 |
|
Heat Deflection Temperature |
|
|
|
|
66 psi, Unannealed | 275 | -- | °F | ISO 75-2/Bf |
264 psi, Unannealed | 122 | -- | °F | ISO 75-2/Af |
Vicat Softening Temperature | 302 | -- | °F | ISO 306/B50 |
Melting Temperature 4 | 428 | -- | °F | ISO 11357-3 |
Surface Resistivity 5 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
Volume Resistivity 5 | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
Comparative Tracking Index(Solution A) | 600 | -- | V | IEC 60112 |
Flame Rating (0.031 in) | HB | -- |
| UL 94 |
Glow Wire Flammability Index (0.08 in) | 1200 | -- | °F | IEC 60695-2-12 |
Flammability (0.12 in) | < 1 | -- | in/min | FMVSS 302 |
Drying Temperature - Desiccant Dryer | 176 | °F |
|
Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr |
|
Dew Point - Desiccant Dryer | -4 | °F |
|
Suggested Max Moisture | 0.15 | % |
|
Processing (Melt) Temp | 482 to 536 | °F |
|
Mold Temperature | 158 to 176 | °F |
|
Injection Rate | Moderate |
|
|