Rynite? 530 NC010
THERMOPLASTIC POLYESTER RESIN
產(chǎn)品說明:
30% Glass Reinforced Polyethylene Terephthalate
填料/增強材料 | |
添加劑 | |
RoHS 合規(guī)性 | |
形式 | |
加工方法 | |
多點數(shù)據(jù) | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Shear Modulus vs. Temperature, Dynamic (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
|
部件標(biāo)識代碼 (ISO 11469) | |
樹脂ID (ISO 1043) | |
密度 | 1.56 | g/cm3 | ISO 1183 |
熔融體積流量（MVR） (280°C/2.16 kg) | 0.305 | in3/10min | ISO 1133 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 0.80 | % |
|
流量 | 0.20 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F, 0.0787 in | 0.70 | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 0.20 | % |
|
粘數(shù) | 55.0 | cm3/g | ISO 307 |
洛氏硬度 |
|
| ISO 2039-2 |
M 計秤 | 100 |
|
|
R 計秤 | 120 |
|
|
拉伸模量 | 1.60E+6 | psi | ISO 527-2 |
拉伸應(yīng)力 (斷裂) | 22900 | psi | ISO 527-2 |
拉伸應(yīng)變 (斷裂) | 2.5 | % | ISO 527-2 |
拉伸蠕變模量 |
|
| ISO 899-1 |
1 hr | 1.57E+6 | psi |
|
1000 hr | 1.28E+6 | psi |
|
彎曲模量 | 1.30E+6 | psi | ISO 178 |
彎曲應(yīng)力 | 33400 | psi | ISO 178 |
泊松比 | 0.34 |
| ISO 527 |
簡支梁缺口沖擊強度 |
|
| ISO 179/1eA |
-40°F | 4.8 | ft·lb/in2 |
|
-22°F | 5.2 | ft·lb/in2 |
|
73°F | 5.2 | ft·lb/in2 |
|
簡支梁無缺口沖擊強度 |
|
| ISO 179/1eU |
-22°F | 21 | ft·lb/in2 |
|
73°F | 29 | ft·lb/in2 |
|
熱變形溫度 |
|
|
|
66 psi, 未退火 | 473 | °F | ISO 75-2/B |
264 psi, 未退火 | 435 | °F | ISO 75-2/A |
維卡軟化溫度 | 446 | °F | ISO 306/B50 |
熔融溫度 3 | 486 | °F | ISO 11357-3 |
線形熱膨脹系數(shù) |
|
| ISO 11359-2 |
流動 | 5.6E-6 | in/in/°F |
|
流動 : -40 到 73°F | 1.2E-5 | in/in/°F |
|
流動 : 131 到 320°F | 2.2E-6 | in/in/°F |
|
橫向 | 4.5E-5 | in/in/°F |
|
橫向 : -40 到 73°F | 3.7E-5 | in/in/°F |
|
橫向 : 131 到 320°F | 5.9E-5 | in/in/°F |
|
導(dǎo)熱系數(shù) | 2.0 | Btu·in/hr/ft2/°F |
|
Effective Thermal Diffusivity | 1.30E-7 | m2/s |
|
表面電阻率 | 1.0E+14 | ohms | IEC 60093 |
體積電阻率 | 1.0E+15 | ohms·cm | IEC 60093 |
介電強度 | 810 | V/mil | IEC 60243-1 |
相對電容率 |
|
| IEC 60250 |
100 Hz | 4.20 |
|
|
1 MHz | 3.80 |
|
|
耗散因數(shù) |
|
| IEC 60250 |
100 Hz | 0.013 |
|
|
1 MHz | 7.0E-3 |
|
|
相比耐漏電起痕指數(shù)(CTI) | PLC 2 |
| UL 746 |
漏電起痕指數(shù) | 250 | V | IEC 60112 |
燃燒速率 4 (0.0394 in) | 1.5 | in/min | ISO 3795 |
UL 阻燃等級 |
|
| UL 94, IEC 60695-11-10, -20 |
0.030 in | HB |
|
|
0.06 in | HB |
|
|
極限氧指數(shù) | 20 | % | ISO 4589-2 |
FMVSS 可燃性 | B |
| FMVSS 302 |
霧化 - G-value (condensate) | 0.0 | g | ISO 6452 |
頂出溫度 | 338 | °F |
|
Emission of Organic Compounds | 16.0 | μgC/g | VDA 277 |
Odor | 3.00 |
| VDA 270 |
干燥溫度 | 248 | °F |
|
干燥時間 - 熱風(fēng)干燥機 | 4.0 到 6.0 | hr |
|
建議的最大水分含量 | 0.020 | % |
|
加工（熔體）溫度 | 536 到 572 | °F |
|
Melt Temperature, Optimum | 545 | °F |
|
模具溫度 | 248 到 284 | °F |
|
Mold Temperature, Optimum | 266 | °F |
|
保壓 | 11600 | psi |
|
Back Pressure | As low as possible |
|
|
Drying Recommended | yes |
|
|
Hold Pressure Time | 4.00 | s/mm |
|
Maximum Screw Tangential Speed | 472 | in/min |
|
如需塞拉尼斯（Celanese）原廠物性表及相關(guān)文件，請聯(lián)系我司工作人員，謝謝！