Rynite? 935 NC010
THERMOPLASTIC POLYESTER RESIN
產(chǎn)品說(shuō)明:
35% Glass Reinforced Polyethylene Terephthalate
填料/增強(qiáng)材料 | |
添加劑 | |
RoHS 合規(guī)性 | |
形式 | |
加工方法 | |
多點(diǎn)數(shù)據(jù) | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Stress vs. Shear Rate (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
|
部件標(biāo)識(shí)代碼 (ISO 11469) | |
樹(shù)脂ID (ISO 1043) | |
密度 | 1.58 | g/cm3 | ISO 1183 |
熔融體積流量（MVR） (280°C/5.0 kg) | 0.305 | in3/10min | ISO 1133 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 0.70 | % |
|
流量 | 0.30 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F, 0.0787 in | 0.83 | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 0.13 | % |
|
洛氏硬度 |
|
| ISO 2039-2 |
M 計(jì)秤 | 75 |
|
|
R 計(jì)秤 | 115 |
|
|
拉伸模量 | 1.48E+6 | psi | ISO 527-2 |
拉伸應(yīng)力 (斷裂) | 12300 | psi | ISO 527-2 |
拉伸應(yīng)變 (斷裂) | 2.0 | % | ISO 527-2 |
拉伸蠕變模量 |
|
| ISO 899-1 |
1 hr | 1.36E+6 | psi |
|
1000 hr | 1.12E+6 | psi |
|
彎曲模量 | 1.32E+6 | psi | ISO 178 |
泊松比 | 0.34 |
| ISO 527 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
| ISO 179/1eA |
-22°F | 1.9 | ft·lb/in2 |
|
73°F | 2.9 | ft·lb/in2 |
|
簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度 |
|
| ISO 179/1eU |
-22°F | 9.5 | ft·lb/in2 |
|
73°F | 12 | ft·lb/in2 |
|
熱變形溫度 |
|
|
|
66 psi, 未退火 | 455 | °F | ISO 75-2/B |
264 psi, 未退火 | 392 | °F | ISO 75-2/A |
維卡軟化溫度 | 401 | °F | ISO 306/B50 |
熔融溫度 3 | 486 | °F | ISO 11357-3 |
線形熱膨脹系數(shù) |
|
| ISO 11359-2 |
流動(dòng) | 8.9E-6 | in/in/°F |
|
流動(dòng) : -40 到 73°F | 1.4E-5 | in/in/°F |
|
橫向 | 2.9E-5 | in/in/°F |
|
橫向 : -40 到 73°F | 2.9E-5 | in/in/°F |
|
Effective Thermal Diffusivity | 1.40E-7 | m2/s |
|
表面電阻率 | 1.0E+14 | ohms | IEC 60093 |
體積電阻率 | 1.0E+15 | ohms·cm | IEC 60093 |
介電強(qiáng)度 | 990 | V/mil | IEC 60243-1 |
相對(duì)電容率 |
|
| IEC 60250 |
100 Hz | 4.50 |
|
|
1 MHz | 4.10 |
|
|
耗散因數(shù) |
|
| IEC 60250 |
100 Hz | 0.030 |
|
|
1 MHz | 0.014 |
|
|
漏電起痕指數(shù) | 300 | V | IEC 60112 |
燃燒速率 4 (0.0394 in) | < 3.9 | in/min | ISO 3795 |
UL 阻燃等級(jí) |
|
| UL 94, IEC 60695-11-10, -20 |
0.030 in | HB |
|
|
0.06 in | HB |
|
|
極限氧指數(shù) | 21 | % | ISO 4589-2 |
FMVSS 可燃性 | B |
| FMVSS 302 |
霧化 - G-value (condensate) | 1.0E-4 | g | ISO 6452 |
熔體密度 | 1.32 | g/cm3 |
|
頂出溫度 | 338 | °F |
|
Specific Heat Capacity of Melt | 0.428 | Btu/lb/°F |
|
Thermal Conductivity of Melt | 2.2 | Btu·in/hr/ft2/°F |
|
干燥溫度 | 248 | °F |
|
干燥時(shí)間 - 熱風(fēng)干燥機(jī) | 4.0 到 6.0 | hr |
|
建議的最大水分含量 | 0.020 | % |
|
加工（熔體）溫度 | 536 到 572 | °F |
|
Melt Temperature, Optimum | 545 | °F |
|
模具溫度 | 212 到 248 | °F |
|
Mold Temperature, Optimum | 230 | °F |
|
保壓 | 11600 | psi |
|
Back Pressure | As low as possible |
|
|
Drying Recommended | yes |
|
|
Hold Pressure Time | 4.00 | s/mm |
|
Maximum Screw Tangential Speed | 472 | in/min |
|
如需塞拉尼斯（Celanese）原廠物性表及相關(guān)文件，請(qǐng)聯(lián)系我司工作人員，謝謝！