Ultramid? A3HG5
聚酰胺66
產品說明:
Ultramid A3HG5 is a 25% glass fiber reinforced injection molding PA66 grade.
Applications
Typical applications include machinery components and housings of high stiffness and dimensional stability.
填料/增強材料 | 玻璃纖維增強材料, 25% 填料按重量 |
特性 | High Dimensional Stability、剛性，高、耐油性能 |
用途 | 機器/機械部件外殼 |
機構評級 | EC 1907/2006 (REACH) |
RoHS 合規性 | RoHS 合規 |
形式 | 粒子 |
加工方法 | 注射成型 |
多點數據 | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2) |
密度 / 比重 |
|
|
|
|
-- | 1.32 | -- |
| ASTM D792 |
-- | 1.32 | -- | g/cm3 | ISO 1183 |
熔融體積流量（MVR） (275°C/5.0 kg) | 3.05 | -- | in3/10min | ISO 1133 |
收縮率 - 流動 (0.125 in) | 3.0E-3 | -- | in/in |
|
吸水率 |
|
|
|
|
飽和 | 6.0 | -- | % | ASTM D570 |
飽和, 73°F | 6.0 | -- | % | ISO 62 |
平衡, 50% RH | 1.9 | -- | % | ASTM D570 |
平衡, 73°F, 50% RH | 1.9 | -- | % | ISO 62 |
拉伸模量 (73°F) | 1.25E+6 | 943000 | psi | ISO 527-2 |
抗張強度 |
|
|
|
|
斷裂, 73°F | 26000 | -- | psi | ASTM D638 |
斷裂, -40°F | 28400 | 27000 | psi | ISO 527-2 |
斷裂, 73°F | 24700 | 17400 | psi | ISO 527-2 |
伸長率 |
|
|
|
|
斷裂, 73°F | 3.0 | -- | % | ASTM D638 |
斷裂, -40°F | 2.9 | 2.7 | % | ISO 527-2 |
斷裂, 73°F | 3.0 | 6.0 | % | ISO 527-2 |
彎曲模量 |
|
|
|
|
73°F | 1.15E+6 | -- | psi | ASTM D790 |
73°F | 1.10E+6 | -- | psi | ISO 178 |
簡支梁缺口沖擊強度 |
|
|
| ISO 179 |
-22°F | 4.3 | -- | ft·lb/in2 |
|
73°F | 4.8 | 8.6 | ft·lb/in2 |
|
簡支梁無缺口沖擊強度 |
|
|
| ISO 179 |
-22°F | 26 | -- | ft·lb/in2 |
|
73°F | 31 | 43 | ft·lb/in2 |
|
懸壁梁缺口沖擊強度 |
|
|
|
|
-40°F | 0.99 | -- | ft·lb/in | ASTM D256 |
73°F | 1.8 | -- | ft·lb/in | ASTM D256 |
73°F | 4.5 | -- | ft·lb/in2 | ISO 180 |
載荷下熱變形溫度 |
|
|
|
|
66 psi, 未退火 | 482 | -- | °F | ASTM D648, ISO 75-2/B |
264 psi, 未退火 | 482 | -- | °F | ASTM D648, ISO 75-2/A |
熔融峰值溫度 | 500 | -- | °F | ASTM D3418, ISO 3146 |
線形熱膨脹系數 |
|
|
|
|
流動 | 5.6E-6 | -- | in/in/°F | ASTM E831 |
流動 | 1.7E-5 | -- | in/in/°F |
|
橫向 | 3.6E-5 | -- | in/in/°F |
|
RTI Elec |
|
|
| UL 746 |
0.031 in | 266 | -- | °F |
|
0.06 in | 266 | -- | °F |
|
0.12 in | 266 | -- | °F |
|
RTI Imp |
|
|
| UL 746 |
0.06 in | 248 | -- | °F |
|
0.12 in | 248 | -- | °F |
|
RTI |
|
|
| UL 746 |
0.06 in | 266 | -- | °F |
|
0.12 in | 266 | -- | °F |
|
體積電阻率 |
|
|
|
|
0.0591 in | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
-- | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
介電常數 (1 MHz) | 3.50 | 5.50 |
| IEC 60250 |
耗散因數 |
|
|
| IEC 60250 |
100 Hz | 0.014 | 0.30 |
|
|
1 MHz | 0.014 | 0.16 |
|
|
漏電起痕指數 | 550 | 550 | V | IEC 60112 |
UL 阻燃等級 |
|
|
| UL 94 |
0.031 in | HB | -- |
|
|
0.06 in | HB | -- |
|
|
0.12 in | HB | -- |
|
|
干燥溫度 | 176 | °F |
|
干燥時間 | 2.0 到 4.0 | hr |
|
建議的最大水分含量 | 0.15 | % |
|
加工（熔體）溫度 | 536 到 581 | °F |
|
模具溫度 | 176 到 194 | °F |
|
注塑壓力 | 508 到 1810 | psi |
|
注射速度 | 快速 |
|
|
如需巴斯夫原廠物性表及相關文件，請聯系我們工作人員，謝謝！