Ultrason? E KR 4113
聚醚砜
產(chǎn)品說明:
Compound based on PES with 30 % filler. The filler system, a mixture of carbon fibres, graphite and PTFE powder, considerably improves Ultrason tribological properties. In addition, this product has a very small expansion coefficient and low tendency to swell in hot oils.
填料/增強(qiáng)材料 | |
機(jī)構(gòu)評(píng)級(jí) | |
RoHS 合規(guī)性 | |
形式 | |
加工方法 | |
樹脂ID (ISO 1043) | |
密度 | 1.48 | g/cm3 | ISO 1183 |
表觀密度 | 0.70 到 0.80 | g/cm3 |
|
溶化體積流率（MVR） (360°C/10.0 kg) | 0.610 | in3/10min | ISO 1133 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 0.46 | % |
|
流量 | 0.31 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F | 1.5 | % |
|
平衡, 73°F, 50% RH | 0.50 | % |
|
粘數(shù) 2 | 56.0 | cm3/g | ISO 307 |
球壓硬度 (H 961/30) | 26100 | psi | ISO 2039-1 |
拉伸模量 | 1.60E+6 | psi | ISO 527-2 |
拉伸應(yīng)力 (斷裂) | 16700 | psi | ISO 527-2 |
拉伸應(yīng)變 (斷裂) | 1.5 | % | ISO 527-2 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
| ISO 179/1eA |
-22°F | 2.4 | ft·lb/in2 |
|
73°F | 3.1 | ft·lb/in2 |
|
簡(jiǎn)支梁無缺口沖擊強(qiáng)度 |
|
| ISO 179/1eU |
-22°F | 9.5 | ft·lb/in2 |
|
73°F | 11 | ft·lb/in2 |
|
懸壁梁缺口沖擊強(qiáng)度 |
|
| ISO 180/A |
-22°F | 2.6 | ft·lb/in2 |
|
73°F | 3.1 | ft·lb/in2 |
|
熱變形溫度 (264 psi, 未退火) | 433 | °F | ISO 75-2/A |
玻璃轉(zhuǎn)化溫度 3 | 437 | °F | ISO 11357-2 |
線形熱膨脹系數(shù) - 流動(dòng) |
|
|
|
73 到 176°F | 6.1E-6 | in/in/°F | ISO 11359-2 |
356°F | 7.2E-6 | in/in/°F | DIN 53752 |
表面電阻率 | 4.0E+3 | ohms | IEC 60093 |
體積電阻率 | 9.0E+5 | ohms·cm | IEC 60093 |
介電強(qiáng)度 | 200 | V/mil | IEC 60243-1 |
干燥溫度 | 284 | °F |
|
干燥時(shí)間 | 4.0 | hr |
|
建議的最大水分含量 | 0.020 | % |
|
料斗溫度 | 176 | °F |
|
料筒后部溫度 | 662 | °F |
|
料筒中部溫度 | 680 | °F |
|
料筒前部溫度 | 698 | °F |
|
射嘴溫度 | 698 | °F |
|
加工（熔體）溫度 | 662 到 734 | °F |
|
模具溫度 | 302 到 374 | °F |
|
Screw Speed | < 709 | in/min |
|